不純物・欠陥制御を用いた非線形光学結晶 CsLiB6O10の紫外レーザー損傷耐性向上

DOI Web Site Web Site 被引用文献1件 参考文献6件

書誌事項

タイトル別名
  • Impurity and Defect Control of Nonlinear Optical Crystal CsLiB6O10 for Improving Ultraviolet Laser-Induced Damage Tolerance
  • Laser Original 不純物・欠陥制御を用いた非線形光学結晶CsLiB₆O₁₀の紫外レーザー損傷耐性向上
  • Laser Original フジュンブツ ・ ケッカン セイギョ オ モチイタ ヒセンケイ コウガク ケッショウ CsLiB ₆ O ₁ ₀ ノ シガイ レーザー ソンショウ タイセイ コウジョウ

この論文をさがす

抄録

We investigated the ultraviolet laser-induced degradation of a nonlinear optical crystal CsLiB6O10 (CLBO). High-repetition-rate 266 nm pulses induced degradation of CLBO at a lower peak power density than the bulk laser-induced damage threshold. This research reveals that the degradation is caused by light-induced refractive index change observed as light-induced lensing effect in LiNbO3. We experimentally estimated the threshold intensity of this degradation. Al-doped CLBO samples have about two times higher threshold (40-50 MW/cm2) than conventional undoped samples (20-30 MW/cm2). We have established growth conditions to obtain high-quality CLBO crystals with lower light scattering. This high-quality crystal can effectively slow down the degradation.

収録刊行物

  • レーザー研究

    レーザー研究 41 (10), 830-, 2013

    一般社団法人 レーザー学会

被引用文献 (1)*注記

もっと見る

参考文献 (6)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ