Organo-Soluble Low CTE Polyimides and their Applications to Photosensitive Cover Layer Materials in Flexible Printed Circuit Boards
-
- Junichi Ishii
- Sony Chemical & Information Device Corporation, 1078 Kamiishikawa, Kanuma, Tochigi, 22-8503, Japan,
-
- Tadashi Akamatsu
- Sony Chemical & Information Device Corporation, 1078 Kamiishikawa, Kanuma, Tochigi, 22-8503, Japan
書誌事項
- 公開日
- 2009-04
- 権利情報
-
- https://journals.sagepub.com/page/policies/text-and-data-mining-license
- DOI
-
- 10.1177/0954008308088397
- 公開者
- SAGE Publications
この論文をさがす
説明
<jats:p> A novel cover layer material for flexible printed circuit (FPC) applications was developed in this work. A high molecular weight of polyimide composed of four monomers, pyromellitic dianhydride (PMDA), 3,3',4,4'-biphenyltetracarboxylic dianhydride (BPDA), 2,2'-bis(trifluoromethyl)benzidine (TFMB) and 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane (BisApAf) was prepared by the one-pot polycondensation in N-methyl-2-pyrrolidone (NMP) without precipitation and gelation. The polyimide (PI) was highly soluble in various common organic solvents. Interestingly, the PI film formed by simple solution-casting of the PI solution had a low CTE value close to that of copper foil, therefore almost no curling of the PI/copper laminate was observed when the PI film was directly formed on a copper foil. The PI film also exhibited other combined properties, including a low CTE, a high T<jats:sub>g</jats:sub>, high thermal stability, low water absorption, comparatively good transparency, the highest levels of non-flammability, good insulation properties and sufficient film flexibility. In addition, fine positive-tone patterns could be obtained from DNQ-containing PI with a sensitivity of 238 mJ cm<jats:sup>-2</jats:sup>. The results revealed that the present PI system is a promising candidate as a novel cover layer material. </jats:p>
収録刊行物
-
- High Performance Polymers
-
High Performance Polymers 21 (2), 123-138, 2009-04
SAGE Publications