Effect of Hf on Microstructure and High-Temperature Strength of a Cast NiAl/Cr(Mo) Alloy

DOI Web Site Web Site 55 References
  • Cui Chuanyong
    Institute of Metal Research, Chinese Academy of Sciences
  • Guo Jianting
    Institute of Metal Research, Chinese Academy of Sciences
  • Qi Yihui
    Institute of Metal Research, Chinese Academy of Sciences
  • Ye Hengqiang
    Institute of Metal Research, Chinese Academy of Sciences

Search this article

Description

A NiAl/Cr(Mo) alloy modified with Hf was fabricated by a vacuum induction melted and drop cast. The alloy was mainly composed of NiAl matrix, Cr(Mo) and Hf-rich phase distributed between NiAl and Cr(Mo) phase boundary and phase transition was also studied. Then it was hot isostically pressed (HIPed) at 1523 K, 200 MPa for 4.5 h. Its high temperature compressive behavior was studied and the deformation features of the alloy could be adequately described by standard power law which is usually used to characterize creep behavior for various metallic material. The stress exponent n as well as the activation energy Q was calculated by fitting the experimental data to the power-law and temperature-compensated power law equation. The possible strengthening mechanism was discussed.

Journal

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 42 (8), 1700-1704, 2001

    The Japan Institute of Metals and Materials

References(55)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top