Corrosion Resistance of Fe-16%Cr-30%Mo-(C,B,P) Amorphous Coatings Sprayed by HVOF and APS Processes
-
- Otsubo Fumitaka
- Department of Materials Science and Engineering, Faculty of Engineering, Kyushu Institute of Technology
-
- Kishitake Katsuhiko
- Department of Materials Science and Engineering, Faculty of Engineering, Kyushu Institute of Technology
書誌事項
- タイトル別名
-
- Corrosion Resistance of Fe 16パーセント Cr30パーセント Mo C B P Amorphous Coatings Sprayed by HVOF and APS Processes
この論文をさがす
抄録
Two kinds of Fe-16%Cr-30%Mo-(C,B,P) alloy powders having high ability to form an amorphous phase were thermal sprayed onto mild steel substrate using HVOF and APS processes. Perfectly amorphous coating was formed not only by the HVOF process but also by the APS process. The passive current densities of the amorphous coatings sprayed by the HVOF and APS processes were close each other and significantly low compared with that of SUS316L coating in 1 mol·L−1 HCl solution. The coatings of perfectly amorphous phase were little corroded after immersion tests in 1 mol·L−1 HCl solution for one week, though the coatings composed of the mixture of amorphous and crystalline phases corroded markedly.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (1), 80-83, 2005
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報
-
- CRID
- 1390001204249823616
-
- NII論文ID
- 10014323637
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2MXit12gtro%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7217983
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可