Analysis on Residual Stress in Electron Beam-Physical Vapor Deposited Thermal Barrier Coating using Hard Synchrotron X-Rays

Bibliographic Information

Other Title
  • 高エネルギー放射光によるEB‐PVD遮熱コーティングの残留応力分布の解析
  • 高エネルギー反射光によるEB-PVD遮熱コーティングの残留応力分布の解析
  • コウエネルギー ホウシャコウ ニ ヨル EB PVDシャネツ コーティング ノ ザンリュウ オウリョク ブンプ ノ カイセキ

Search this article

Abstract

The distribution of the residual stress in the thermal barrier coating, which was made by an electron beam-physical vapor deposition (EB-PVD) method, was determined using X-ray stress measurements. As the bond coating, NiCoCrAlY was low-pressure plasma sprayed on the substrate of austenitic stainless steel. The 8 mass% Y2O3-ZrO2 was coated on the bond coating using the EB-PVD method as the top coating. The top coating had the preferred orientation with the <111> axis direction perpendicular to the coating plane. The distribution of the in-plane residual stress in the top coating was measured using laboratory X-rays. The value of the in plane stresses was deter-mined by the sin2 φ method after the separation of the 133 and 331 diffractions. The distribution of the out-of-plane strain in the top coating was measured using the strain scanning method with hard synchrotron X-rays. The out-of-plane strain was obtained from the 333 diffraction which had strong intensity due to the preferred orientation. The measured value of the in-plane stress in the top coating was a large compression, and steeply decreased near the interface between the top and the bond coating. The distribution of the out-of-plane stress showed a compression, and its magnitude was smaller than that of the in-plane stress.

Journal

Citations (3)*help

See more

References(14)*help

See more

Related Projects

See more

Details

Report a problem

Back to top