高エネルギー反射光によるEB-PVD遮熱コーティングの残留応力分布の解析
書誌事項
- タイトル別名
-
- Analysis on Residual Stress in Electron Beam-Physical Vapor Deposited Thermal Barrier Coating using Hard Synchrotron X-Rays
- 高エネルギー放射光によるEB‐PVD遮熱コーティングの残留応力分布の解析
- コウエネルギー ホウシャコウ ニ ヨル EB PVDシャネツ コーティング ノ ザンリュウ オウリョク ブンプ ノ カイセキ
この論文をさがす
抄録
The distribution of the residual stress in the thermal barrier coating, which was made by an electron beam-physical vapor deposition (EB-PVD) method, was determined using X-ray stress measurements. As the bond coating, NiCoCrAlY was low-pressure plasma sprayed on the substrate of austenitic stainless steel. The 8 mass% Y2O3-ZrO2 was coated on the bond coating using the EB-PVD method as the top coating. The top coating had the preferred orientation with the <111> axis direction perpendicular to the coating plane. The distribution of the in-plane residual stress in the top coating was measured using laboratory X-rays. The value of the in plane stresses was deter-mined by the sin2 φ method after the separation of the 133 and 331 diffractions. The distribution of the out-of-plane strain in the top coating was measured using the strain scanning method with hard synchrotron X-rays. The out-of-plane strain was obtained from the 333 diffraction which had strong intensity due to the preferred orientation. The measured value of the in-plane stress in the top coating was a large compression, and steeply decreased near the interface between the top and the bond coating. The distribution of the out-of-plane stress showed a compression, and its magnitude was smaller than that of the in-plane stress.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 71 (711), 1523-1529, 2005
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報
-
- CRID
- 1390001204478691200
-
- NII論文ID
- 110004999113
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD28XhtlGrurk%3D
-
- ISSN
- 18848338
- 03875008
-
- HANDLE
- 2237/9130
- 10191/5715
-
- NDL書誌ID
- 7741676
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可