- Effect of Composition on Mechanical Properties of β-Sialon
- ベータ サイアロン ノ ソセイ ニ ヨル キョウド トクセイ
この論文をさがす
説明
The preparation of β-sialon from a powder mixtures of Si3N4, Al2O3 and AlN was studied with respect to the media and duration of ball milling and the particle size of Al2O3. The mechanical properties of hot-pressed β-sialon with z=1, 2, 3 and 4 were measured. The distribution of flexural strength was smallest after 72h milling. The effect of the average particle size of Al2O3 (<1μm) on the flexural strength was not clear. The flexural strength and Vickers hardness of β-sialon decreased from about 50kg/mm2 to about 38kg/mm2 and from about 2100kg/mm2 to about 1300kg/mm2, respectively, with increasing z-value from 1 to 4. Young's modulus decreased from 2.91×106kg/cm2 to 2.34×106kg/cm2 with increasing z-value from 1 to 3, howerver, it increased slightly to 2.37×106kg/cm2 at z=4. Fracture toughness decreased from about 3.6MN/m3/2 to about 2.4MN/m3/2 with increasing z-value from 1 to 3, and it was almost constant from z=3 to z=4.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 93 (1079), 370-375, 1985
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205249858432
-
- NII論文ID
- 110002313407
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3044634
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可