一方向強化ＡＳ４／ＰＥＥＫ積層板の高温下における混合モードクリープ層間はく離き裂進展

DOI 機関リポジトリ 機関リポジトリ (HANDLE) Web Site 参考文献25件

書誌事項

タイトル別名
  • Mixed Mode Delamination Creep Crack Growth of Unidirectionally Reinforced AS4/PEEK Laminate at Elevated Temperature.
  • イチ ホウコウ キョウカ AS4 PEEK セキソウバン ノ コウオン カ ニ オケル コンゴウ モードクリープソウ カン ハクリ キレツ シンテン

この論文をさがす

説明

Mixed mode I+II delamination crack growth tests at elevated temperature (473K) were carried out on unidirectionally carbon fiber reinforced thermoplastics (CFRTP) under static creep condition. Asymmetric end loaded split (AELS) specimens were used in order to investigate the effect of mixed mode ratio, GI/GII, on crack growth. The creep crack growth rate, da/dt, became higher in terms of mode I component of total energy release rate, GI, as GI/GII decreased. This implies that the crack propagation rate was accelerated by mode II component, GII. The measurement of the load point displacement rates due to mode I or mode II component of total load revealed that the creep deformation at the crack tip by mode II component was larger than that by mode I component and the size of creep deformation area depended on GI/GII. It is considered that the creep deformation by mode I component, which was perpendicular to carbon fibers, was constrained strongly by fibers, while the creep deformation by mode II expanded along carbon fibers. The crack growth rate under mixed mode loading was governed by the creep J integral, J, regardless of the mixed mode ratio. Fractographic observation showed that matrices were elongated along carbon fibers and fracture occurred at the interface between fibers and matrix.

収録刊行物

  • 材料

    材料 50 (11), 1255-1261, 2001

    公益社団法人 日本材料学会

参考文献 (25)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ