圧縮変形したステンレス鋼巻線の焼結挙動

DOI Web Site

書誌事項

タイトル別名
  • Sintering of Wire-wound Compacts after Pressing and Deformation.
  • アッシュク ヘンケイシタ ステンレス コウマキセン ノ ショウケツ キョドウ

この論文をさがす

説明

18 Cr-8 Ni stainless steel wires 0.160mm and 0.035mm in diameters were wound in layers on core rods of the same steel. Before sintering in hydrogen, the wire layers were cold-pressed in the direction along core axis to form flat contact areas between wires, with widths of one third of the each original wire diameter. Welds between contacting surfaces of wires were observed on sections of the wire layers by optical and scanning-electron microscopes.<BR>The initial stage of sintering begins by the formation of micro welds at some points between contacting surfaces. The welds grow and coalesce with each other eliminating micro pores between them to occupy whole the flat contacts between wires. The activation energy of welding 60% of the flat area is lower than that for grain boundary diffusion of iron in a stainless steel. The energy of welding 90% is similar to that for volume diffusion. Welding rates during the initial stage of sintering are independent on wire diameter. The growth of a whole neck proceeds more rapidly between smaller wires than between larger ones. Curvatures of the necks are independent on wire diameter.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ