- The Formability and Texture of High-density Sintered Iron Sheets Annealed after Cold-rolling
- レイエン ゴ ショウドン シタ コウミツド ショウケツ テッパン ノ セイケイセイ ト ソノ シュウゴウ ソシキ ニ ツイテ
この論文をさがす
説明
The formability of high-density iron sheets, sintered at 850°C for 4 hours in hydrogen, subsequently coldrolled, and annealed in a two-stage process, was examined by using the Erichsen cupping test, the deep drawing test, and r-value measurement. The annealing textures of the iron sheets were also investigated by means of an X-ray pole figure method and magnetic torque curve analysis. The results obtained are summarized as follows: (1) The formability of high-density sintered iron sheets in this study was similar to that of low carbon iron sheets. (2) The high-density sintered iron sheets which were reduced within the range of 85% to 90% by the secondary cold-rolling before annealing, were mechanically isotropic in the sheet plane. (3) The annealing textures of high-density sintered iron sheets which were mechanically isotropic in the sheet plane, showed that the intensity of (111) [112] and (211) [011] orientations was strong, whereas that of (110) [001] and (110) [110] orientations was weak, and the (100) [011], (100) [012] and (311) [136] orientations appeared slightly in the texture of the sheets.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 20 (8), 255-260, 1974
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206307902976
-
- NII論文ID
- 130000816643
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 7641970
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可