- Effect of Annealing Temperature on Texture Formation of Ti-4Au-5Cr-8Zr Biomedical Superelastic Alloy
- Ti-4Au-5Cr-8Zr セイタイヨウ チョウダンセイ ゴウキン ノ シュウゴウ ソシキ ケイセイ ニ オヨボス ショウドン オンド ノ エイキョウ
- 公開日
- 2015
- 資源種別
- journal article
- DOI
-
- 10.2320/jinstmet.jb201516
- 公開者
- 公益社団法人 日本金属学会
この論文をさがす
説明
The effect of annealing temperature on texture formation associated with superelastic behavior is clarified of Ti-4Au-5Cr-8Zr biomedical alloy in which Ti3Au precipitates at 973 K and 1073 K but does not precipitate at 1173 K. A Ti-4Au-5Cr-8Zr alloy ingot was cold-rolled with a reduction up to 98% in thickness followed by annealing at 973, 1073 and 1173 K for 1.8 ks. It was found that the as-rolled alloy and the alloy annealed at 973 K exhibit {112}β〈110〉β rolling texture, while the alloys annealed at 1073 K and 1173 K exhibit {001}β〈110〉β recrystallization texture regardless of Ti3Au precipitates. {001}β〈110〉β texture develops stronger in the alloy annealed at 1173 K compare with the alloy annealed at 1073 K. This is one of the reasons why alloy annealed at 1173 K shows larger shape recovery strain than the alloy annealed at 1073 K when tensile strain is applied along the rolling direction.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 80 (1), 45-50, 2015
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481797248
-
- NII論文ID
- 130005115560
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 027051570
-
- 本文言語コード
- ja
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可