書誌事項
- タイトル別名
-
- Effect of Al and Cu Contents on Mechanical Properties of Au-Cu-Al Shape Memory Alloys
- Au-Cu-Alケイ ケイジョウ キオク ゴウキン ノ キカイテキ セイシツ ニ オヨボス Al オヨビ Cu ノウド ノ エイキョウ
- 公開日
- 2015
- 資源種別
- journal article
- DOI
-
- 10.2320/jinstmet.jb201511
- 公開者
- 公益社団法人 日本金属学会
この論文をさがす
説明
In order to develop high performance biomedical shape memory alloy having both good biocompatibility and high X-ray radiography resolution, effects of Al and Cu contents on the martensitic transformation, microstructure and mechanical properties of AuCuAl ternary alloys were studied. Differential scanning calorimetry revealed that the martensitic transformation start temperature decreased with a rate of −7 K/mol%Al in the Au-30 mol%Cu-Al alloys. Besides, the Ms increased with a rate of 18~53 K/mol%Cu in the Au-Cu-15~20 mol%Al alloys in the Cu-poor side of stoichiometry, while the Ms was almost constant in Cu-rich side. By taking into account of the estimated defect structures, the number of Au-Al atomic bonds is important for the stabilization of the parent β phase. Corresponding microstructural change due to the martensitic transformation was confirmed by optical microscopy. Vickers hardness of the Au-30 mol%Cu-Al alloys decreased with increasing Al content, and a minimum was reached at 20~25 mol%Al and then the Vickers hardness increased at 25 mol%Al. The alloys at a limited composition range around Au-30~31 mol%Cu-14~15 mol%Al possessed both high strength and ductility in addition to pseudoelasticity, while the other alloys exhibited poor ductility.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 80 (1), 27-36, 2015
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206481802240
-
- NII論文ID
- 130005115567
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 027051530
-
- 本文言語コード
- ja
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可