細線伸線材の表層部付加的せん断ひずみ層における<br>内部組織と引張り強さ向上の関係

書誌事項

タイトル別名
  • Relationship between Microstructure of Additional Shear Strain Layer<br>and Increase in Tensile Strength of Finely Drawn Wire
  • サイセン シンセンザイ ノ ヒョウソウブ フカテキ センダン ヒズミソウ ニ オケル ナイブ ソシキ ト ヒッパリ ツヨサ コウジョウ ノ カンケイ ヒキヌキザイ ニ オケル ヒョウソウブ フカテキ センダン ヒズミソウ ノ ケンキュウ ダイ2ホウ
  • — Additional Shear Strain Layer at Surface of Drawn Wire II —
  • — 引抜き材における表層部付加的せん断ひずみ層の研究 第2報 —

この論文をさがす

抄録

Fine wires (with a diameter less than 0.4 mm) have been extensively used for precision machines and other devices. It is well known that finely drawn wires have a much higher tensile strength than thick drawn wires. In the drawing process, a large shear deformation zone with a hardened layer, known as the “additional shear strain layer”, is generated beneath the surface layer of the wire. It was clarified that the depth of this additional shear strain layer was about 0.04 mm for wires of various diameters. As the diameter becomes small, the area ratio of the additional shear layer increases. Hence, the additional shear strain layer is a factor contributing to the high tensile strength of fine wires. In this paper, the main purpose is to discuss the cause of the increase in the tensile strength of the additional shear strain layer metallurgically. Thus, the crystal orientation and microstructure was measured by the Electron Back-Scatter Diffraction (EBSD) method. It was ascertained that the crystal of the surface layer was subdivided more finely than the center, and then the tensile strength of the surface layer increased.

収録刊行物

  • 塑性と加工

    塑性と加工 49 (568), 409-413, 2008

    一般社団法人 日本塑性加工学会

被引用文献 (4)*注記

もっと見る

参考文献 (13)*注記

もっと見る

関連プロジェクト

もっと見る

詳細情報

問題の指摘

ページトップへ