Thermal and Mechanical Properties of Cu-Based Cu-Zr-Ti Bulk Glassy Alloys

DOI DOI Web Site Web Site Web Site ほか1件をすべて表示 一部だけ表示 被引用文献46件 参考文献44件 オープンアクセス

書誌事項

タイトル別名
  • Thermal and Mechanical Properties of Cu-Based Cu-Zr-Ti-Y Bulk Glassy Alloys
公開日
2001
DOI
  • 10.2320/matertrans.42.2042
  • 10.2320/matertrans.42.1149
公開者
公益社団法人 日本金属学会

この論文をさがす

説明

A new Cu-based bulk glassy alloy with high tensile fracture strength above 2000 MPa was formed in a (Cu0.6Zr0.3Ti0.1)98Y2 alloy by copper mold casting. The maximum sample thickness for glass formation is 4 mm for Cu60Zr30Ti10 and increases to 5 mm for the 2%Y-containing alloy. The addition of 2%Y also causes an increase in the supercooled liquid region (ΔTx=Tx−Tg) from 36 to 50 K and in the reduced glass transition temperature (Tg⁄Tl) from 0.62 to 0.63. The increase in the glass-forming ability (GFA) is presumably due to the increase in ΔTx and Tg⁄Tl. The bulk glassy (Cu0.6Zr0.3Ti0.1)98Y2 alloy exhibits good mechanical properties, i.e., 1780 MPa for yield strength, 2030 MPa for tensile fracture strength, 2100 MPa for compressive fracture strength, 1.7% for elastic elongation and 1.5% for plastic elongation. The distinct plastic elongation indicates good ductile nature of the Cu-based bulk glassy alloy. The success of synthesizing the new Cu-based bulk glassy alloy with high GFA and good mechanical properties allows us to expect the extension of application fields as a new engineering material.

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 42 (10), 2042-2045, 2001