Chromophore Effect of Non-ionic Photoacid Generators on Resist Performances
-
- Nishimae Yuichi
- Technology Center Electronic Materials, Coating Effects Segment, Ciba Japan K.K.
-
- Yamato Hitoshi
- Technology Center Electronic Materials, Coating Effects Segment, Ciba Japan K.K.
-
- Asakura Toshikage
- Technology Center Electronic Materials, Coating Effects Segment, Ciba Japan K.K.
-
- Ohwa Masaki
- Technology Center Electronic Materials, Coating Effects Segment, Ciba Japan K.K.
この論文をさがす
説明
So far, we have developed and reported a series of novel oxime sulfonate type of photoacid generators (PAG) composed of a fluorenyl chromophore like 2-[2,2,3,3,4,4,5,5-octafluoro-1-(nonafluorobutylsulfonyloxyimino)-pentyl]-fluorene (ONPF), which generates a strong acid (nonaflic acid) by light irradiation and is promising for chemically amplified ArF photoresists. They generate a fluorinated alkylsulfonium acid as a strong acid, have high transparency at 193 nm, and show higher hydrophobicity than TPSnf, good solubility in various solvents, and good thermal stability. However, it has been observed that such fluorenyl PAGs did not have a good coating property, and showed a few striation patterns after spin-coating of some formulations. To improve the striation issue while keeping the desirable properties, replacement of the chromophore was examined, and it has been revealed that 8-[2,2,3,3,4,4,5,5-octafluoro-1-(nonafluorobutylsulfonyloxyimino)-pentyl]-fluoranthene (PAG A) composed of a fluoranthenyl chromophore and 4''-[2,2,3,3,4,4,5,5-octafluoro-1-(nonafluorobutylsulfonyloxyimino)-pentyl]-[1,1',4',1'']terphenyl (PAG B) could dramatically improve the coating property and the P-parameter was comparable to that of ONPF. This improvement is due to enhancement of compatibility toward a polymer matrix composed of high carbon content. Therefore, it has been observed that higher carbon content in a PAG molecule provides better coating property.
収録刊行物
-
- Journal of Photopolymer Science and Technology
-
Journal of Photopolymer Science and Technology 21 (3), 377-381, 2008
フォトポリマー学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679300755072
-
- NII論文ID
- 130004464668
- 40016108995
-
- NII書誌ID
- AA11576862
-
- COI
- 1:CAS:528:DC%2BD1cXosVKqsLw%3D
-
- ISSN
- 13496336
- 09149244
-
- NDL書誌ID
- 9548774
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可