Preparation and Properties of Polyamides by Ring-opening Polyaddition Reaction of N, N'-Bis(ethoxycarbonyl)pyromellitimide with Aromatic Diamines

DOI Web Site
  • IMAI Yoshio
    Department of Polymer Chemistry, Faculty of Engineering, Yamagata University
  • ABE Takashi
    Department of Polymer Chemistry, Faculty of Engineering, Yamagata University

Bibliographic Information

Other Title
  • N,N'-ビス(エトキシカルボニル)ピロメリトイミドと芳香族ジアミンの開環重付加反応によるポリアミドの合成およびその性質

Search this article

Description

Polyamides were prepared by the ring-opening polyaddition reaction of N, N'-bis(ethoxycarbonyl)pyromellitimide with bis(4-aininophenyl) ether (ODA) and other aromatic diamines in N-methyl-2-pyrrolidone (NMP). The preparation of high molecular weight polymer required high monomer concentration and a longer reaction time such as over 5 days at room temperature. When the reaction temperature was raised to 70° C, gelation was occurred due to the partial imidization of the resulting polyamide, along with the increase of the rate of polymerization. The polyamide having the highest viscosity was obtained from ODA among the aromatic diamines. Tetrahydrofuran was not satisfactory as reaction medium, because the polymer was precipitated from the reaction mixture during the polymerization. The polyamide solution in NMP showed good hydrolytic stability against the contact of water. DTA curve of the polyamide exhibited an endothermic peak at 160° C, which is attributable to elimination of urethane during polyimide formation. The behavior was also supported by TGA.

Journal

  • NIPPON KAGAKU KAISHI

    NIPPON KAGAKU KAISHI 1972 (10), 1922-1925, 1972-10-10

    The Chemical Society of Japan