- Nanoscopic Strength Analysis of Tempered-Martensitic Steels.
- ヤキモドシ マルテンサイト コウ ノ ナノ リョウイキ キョウド カイセキ
この論文をさがす
説明
The relationships between tensile strength and microstructural parameters and between fatigue limit and microstructural parameters were investigated for seven tempered-martensitic steels S45C, SMn443, SCr440, SNCM439, SCM440, SUP7 and SUP12. An optical and atomic force microscopy showed that prior-austenitic grain diameter, dγ, block width, Wblo, and precipitation spacing, λ, were 18μm, 0.7μm and 0.11∼0.24μm, respectively, as microstructural parameters. A nanoindentation showed that HV=100+Hv*dls+Hv*pre+Hv*bou, where Hv is macro-Vickers hardness, and Hv*pre and Hv*bou are micro-covered Vickers hardness due to dislocation and solid, precipitation and block boundary strengthening. Hv*pre and Hv*bou were expressed by the microstructural parameters of λ and Wblo. The constant value of 100 is base hardness of the iron. Based on these results, we proposed that tensile strength σB and fatigue limit σw, were expressed in the followings. σB=3.27{100 + Hv*dls + 1.02 × 10-2λ-1 + 3.67 × 10-4λ-1w-1/2blo}…………………………………(A-1) σw=1 .6{100 + Hv*dls + 1.02 × 10-2λ-1 + 1.15(3.67 × 10-4λ-1w-1/2blo)}…………………………(A-2)
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 68 (674), 1473-1480, 2002
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679424165376
-
- NII論文ID
- 110002370242
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- NDL書誌ID
- 6330486
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可