Mechanical properties and microstructures of dental cast Ti-6Nb-4Cu, Ti-18Nb-2Cu, and Ti-24Nb-1Cu alloys
-
- TAKAHASHI Masatoshi
- Division of Dental Bioaterials, Tohoku University Graduate School of Dentistry
-
- TAKADA Yukyo
- Division of Dental Bioaterials, Tohoku University Graduate School of Dentistry
-
- KIKUCHI Masafumi
- Department of Biomaterials Science, Kagoshima University Graduate School of Medical and Dental Sciences
書誌事項
- 公開日
- 2016
- 資源種別
- journal article
- DOI
-
- 10.4012/dmj.2015-354
- 公開者
- 一般社団法人 日本歯科理工学会
この論文をさがす
説明
<p>The mechanical properties —tensile strength, yield strength, elongation after fracture, and Vickers hardness— and alloy phases of the dental cast alloys Ti-6%Nb-4%Cu, Ti-18%Nb-2%Cu, and Ti-24%Nb-1%Cu were investigated. Ti-6%Nb-4%Cu consisted of a single α-phase, while Ti-18%Nb-2%Cu and Ti-24%Nb-1%Cu consisted of α- and β-phases. The tensile strengths, yield strengths, and hardnesses of these alloys were higher than those of Ti-5%Cu and Ti-30%Nb; however, their breaking elongations were smaller. These differences in the mechanical properties are attributable to solid-solution strengthening or to precipitation strengthening by the dual-phase (α+β) structure. Thus, Ti-Nb-Cu alloys are suitable for use in high-strength dental prostheses, such as implantretained superstructures and narrow-diameter implants.</p>