Corrosion resistance of alumina-magnesia castable to slag in steel ladle lining
-
- SADATOMI Yoshitaka
- Technical Research Laboratories, Krosaki Harima Corporation
-
- ENOMOTO Naoya
- Department of Applied Chemistry, Faculty of Engineering, Kyushu University
-
- HOJO Junichi
- Department of Applied Chemistry, Faculty of Engineering, Kyushu University
書誌事項
- 公開日
- 2011
- DOI
-
- 10.2109/jcersj2.119.916
- 公開者
- 公益社団法人 日本セラミックス協会
この論文をさがす
説明
The corrosion resistance of alumina-magnesia castable to a basic slag was evaluated to find the highly-resistive castable composition for steel processing. Stable solid phases were CA6, alumina and spinel after firing of the castable of Al2O3–MgO–CaO–SiO2 system. The slag corrosion was simulated thermodynamically for CA6, alumina, spinel and castables. The solubility of each oxide component is expected in the order of MgAl2O4 > CA6 > Al2O3 at 1600°C because of the formation of CA2 on CA6 and the formation of CA2 and CA6 on alumina, suggesting the protection of castable from slag. However, CA2 and CA6 disappear at 1800°C and the solubility changes in the order of CA6 > Al2O3 > MgAl2O4. Although the protection of castable by CA6 is also expected, the CA6 disappears at a large amount of slag and a high temperature. The solubility of castable decreases with increasing MgO/CaO ratio owing to spinel formation. The practical immersion test demonstrated the high corrosion resistance of high MgO/CaO castable against slag, exhibiting the importance of spinel formation.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 119 (1396), 916-921, 2011
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680264436736
-
- NII論文ID
- 130002067667
-
- ISSN
- 13486535
- 18820743
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可