平滑材および切欠き材に対するプログラム変動荷重による累積疲労被害

DOI Web Site

書誌事項

タイトル別名
  • Cumulative Fatigue Damage under Loading of Programmed Alternating Stresses
  • ヘイカツザイ オヨビ キリカキ ザイ ニ タイスル プログラム ヘンドウ カジュウ ニ ヨル ルイセキ ヒロウ ヒガイ

この論文をさがす

説明

A report is given at the outset of a modified rotating-bending fatigue testing machine by means of which the specimens can be submitted to programmed alternating stress cycles. The test material is mild steel with 0.47% C which was annealed in vacuum after machining. The results of the tests are reported, of the plain specimens and of four sorts of notched specimens, and the accumulation of the fatigue damage is discussed.<br>It is shown that with the plain specimens and with the blunt notched specimens Miner's hypothesis concerning “linear damage law” that the stress cycles are negligible so far as their amplitude is less than the fatigue limit of the specimen in question could agree with the experimental results. But with the specimens with notches the value of whose stress concentrations factor is larger than 1.8 their fatigue life is found in estimation remarkably critical under “the linear damage law”.

収録刊行物

  • 材料

    材料 17 (173), 84-88, 1968

    公益社団法人 日本材料学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ