Use of Ultrasonic Vibration to Wet-Chemical Powder Processing
-
- ENOMOTO Naoya
- Kyushu University, Department of Applied Chemistry, JAPAN
-
- YAMADA Kosuke
- Kyushu University, Department of Applied Chemistry, JAPAN
-
- KUMAGAI Akihiro
- Kyushu University, Department of Applied Chemistry, JAPAN
-
- UEHARA Masato
- Kyushu University, Department of Applied Chemistry, JAPAN
-
- HOJO Junichi
- Kyushu University, Department of Applied Chemistry, JAPAN
説明
Strong and subtle ultrasound was applied to a reacting solution and a starting solution, respectively, for ceramic powder preparation. The magnetite precipitation involves the dissolution of the initial precipitate of Fe(OH)2, the oxidation of Fe2+ to Fe3+, and the nucleation & growth. Effect of ultrasound was separatedly discussed at each stage. Two methods of ultrasonication, i.e., travelling wave and standing wave, were compared. Conspicuous difference of the two methods appeared when the initial concentration of Fe(OH)2, which decreases the particles size of magnetite, is as low as 0.001mol/l. That is, magnetite particles could not be formed under a strong macroscopic flow, even that made by a magnetic stirrer. However, 10nm-sized magnetite was successfully prepared by the standing wave treatment. Aparent transparency of a starting solution may include microscopic inhomogeneity which could be modified by aging or subtle ultrasonication. Effect of them on ceramic particles synthesis is discussed.
収録刊行物
-
- 日本セラミックス協会 年会・秋季シンポジウム 講演予稿集
-
日本セラミックス協会 年会・秋季シンポジウム 講演予稿集 2003F (0), 26-26, 2003
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680589170304
-
- NII論文ID
- 130006968449
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可