Effect of Surface Treatments on Dispersibility and EPD Behavior of Fine SiC Powder in Aqueous Suspensions

DOI
  • ZHOU Yang
    Department of Applied Chemistry, Faculty of Engineering, Kyushu University, JAPAN
  • HONDA Akiko
    Department of Applied Chemistry, Faculty of Engineering, Kyushu University, JAPAN
  • TAKEDA Tomokazu
    Department of Applied Chemistry, Faculty of Engineering, Kyushu University, JAPAN
  • UEHARA Masato
    Department of Applied Chemistry, Faculty of Engineering, Kyushu University, JAPAN
  • ENOMOTO Naoya
    Department of Applied Chemistry, Faculty of Engineering, Kyushu University, JAPAN
  • HOJO Junichi
    Department of Applied Chemistry, Faculty of Engineering, Kyushu University, JAPAN

書誌事項

公開日
2003
DOI
  • 10.14853/pcersj.2003f.0.64.0
公開者
公益社団法人 日本セラミックス協会

説明

Surface treatments, such as calcination, acid solution leaching and alkali solution leaching, were used to improve the dispersibility and increase the electrophoretic deposition (EPD) weight for a fine SiC powder. Main impurities including hydrophobic free carbon, hydrocarbon and fluorine ion on the particle surface caused the low dispersibility and less deposition for the as-received powder in aqueous suspension. After calcination, the dispersibility and deposition weight were enhanced obviously. Acid leaching and alkali leaching were more effective to eliminate these impurities. The deposition weights of the two kinds of powders were about 4 times larger than that of the as-received powder. Slight oxidation on the particle surface after acid leaching led to the largest deposition weight for the acid leached powder. The reason for the improvement caused by different treatments was discussed according to the results of zeta potential, FTIR, XPS analyses and ion conductivity test.

収録刊行物

詳細情報 詳細情報について

  • CRID
    1390282680590608000
  • NII論文ID
    130006969934
  • DOI
    10.14853/pcersj.2003f.0.64.0
  • 本文言語コード
    en
  • データソース種別
    • JaLC
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ