Synthesis of New Mono-Carbonitride(W,Mo)(C,N) Powder by Heating W-Mo Alloy+C Mixed Powder in High-Pressure Nitrogen Gas.
-
- Asada Nobuaki
- Allied Material Corp., Ltd.
-
- Yamamoto Yoshiharu
- Allied Material Corp., Ltd.
-
- Igarashi Tadashi
- Formerly, Tokyo Tungsten Co., Ltd.
-
- Doi Yoshihiko
- Allied Material Corp., Ltd.
-
- Hayashi Koji
- Institute of Industrial Science, The University fo Tokyo
この論文をさがす
説明
We have already succeeded in synthesizing new mono-carbonitrides W (C, N) and Mo(C, N) with 11-20at%N and 14-25at%N respectively by heating W+C and Mo+C mixed powder in high-pressure N2 gas of 10-160MPa at 1523-1673K. In this study, the synthesis of new (W, Mo)(C, N) powder was tried by heating W+Mo+C mixed elemental powder and W-Mo solid solution alloy+C mixed powder in such high-pressure-N2gas. (W, Mo)(C, N) with N content of 14-24at% could be synthesized at 25 -160MPa in case of (W-Mo)+C mixed powder (Metal/C atomic ratio is 1/1), while (W, Mo)(C, N) could not in case of W+Mo+C mixed elemental powder.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 49 (4), 270-278, 2002
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681283528576
-
- NII論文ID
- 10008222527
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 6146152
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可