陽電子消滅分光法を用いた中性子照射したＮｉ‐Ｓｎ合金中のＳｎ原子と原子空孔の相互作用
書誌事項
- タイトル別名
-
- Interaction between Sn Atoms and Vacancies in Neutron-Irradiated Ni-Sn Alloys by Positron Annihilation Spectroscopy
- 陽電子消滅分光法を用いた中性子照射したNi-Sn合金中のSn原子と原子空孔の相互作用
- ヨウデンシ ショウメツ ブンコウホウ オ モチイタ チュウセイシ ショウシャ シタ Ni Sn ゴウキン チュウ ノ Sn ゲンシ ト ゲンシ クウコウ ノ ソウゴ サヨウ
この論文をさがす
説明
Solute atoms greatly influence irradiation damage structures. For example, voids are formed in pure Ni at 573 K, but they are not formed in Ni-Sn alloys irradiated by fission neutrons at 573 K to 0.2 dpa. In this study, the interaction between solute atoms and vacancies and correlation between void growth and solute atoms in neutron-irradiated Ni-Sn alloys were investigated by positron annihilation spectroscopy. Positron annihilation lifetime measurements showed that void density was lower in Ni-0.05 at%Sn than pure Ni. In Ni-0.3 at%Sn, single vacancies, di-vacancies and small stacking fault tetrahedra (SFTs) were formed and the size did not change below 0.1 dpa. In Ni-2 at%Sn, single vacancies and SFTs were formed and the size also did not change below 0.1 dpa. In Ni-Sn alloys, the total intensities of lifetime related to vacancy type defects were more than 60%. Vacancy concentration was higher than in pure Ni and a large number of positrons annihilated at them. From positron annihilation coincidence Doppler broadening (CDB) measurements, the ratio of annihilation of positrons and low-momentum electrons increased in Ni-Sn alloys compared with pure Ni. The ratio increased with increasing the solute atom concentration. As positron affinity of Sn is lower than that of Ni, positrons are attracted to Sn atoms more strongly than Ni. Complexes of vacancy clusters and Sn atoms are formed and the number of Sn atoms adjacent to vacancy clusters increases with the solute atom concentration. It is expected that Sn atoms change the electron state of vacancy clusters, which leads to the increase of annihilation ratio between positrons and low-momentum electrons.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 74 (9), 572-577, 2010
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681453740160
-
- NII論文ID
- 10026599417
-
- NII書誌ID
- AN00062446
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- HANDLE
- 2433/146515
- 2433/171904
-
- NDL書誌ID
- 10804515
-
- 本文言語コード
- ja
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- IRDB
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可