- Electron beam sensitivities and thermal properties of heat-treated poly(methyl methacrylate-co-t-butyl methacrylate)s.
- ネツ ショリシタ ポリ メタクリルサン メチル co メタクリルサン t ブチ
この論文をさがす
説明
The relation of monomer ratios in poly (methyl methacrylate-co-t-butyl methacrylate) s to electron beam sensitivities and thermal properties of the heat-treated copolymers was investigated in order to develop a highly sensitive positive electron beam resist. These copolymers sustained weight loss as a result of heat-treatment at 250°C and the evolved gases during this heat-treatment were mainly composed of isobuten. Therefore this weight loss was due to elimination of the t-butyl groupsfrom the t-butyl methacrylate component in the copolymers. Cyclized acid anhydrides mainly formed on such portions of the heat-treated copolymer films. The glass transition temperature of the copolymers increases as a result of the heat-treatment, so that thermal stabilities were improved, with a higher content of t-butyl methacrylate in the copolymers. In these copolymers, a 37 mol%. composition of t-butyl methacrylate, designated CP-3-2, showed the highest sensitivity (0.35 μC/cmcm2) and a high γ-value (1.9). Moreover, the CP-3-2 resolved a micro circuit pattern (less than 1.0μm line width), and the resistance to dry etching of the CP-3-2 are higher than the values for poly (methyl methacrylate). It is clear that CP-3-2 has a higher performance for highly sensitive positive electron beam resist.
収録刊行物
-
- 高分子論文集
-
高分子論文集 43 (3), 153-160, 1986
公益社団法人 高分子学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681500758656
-
- NII論文ID
- 130003837005
-
- NII書誌ID
- AN00085011
-
- ISSN
- 18815685
- 03862186
-
- NDL書誌ID
- 3069544
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可