低放射化フェライト鋼のクリープに伴う水素昇温脱離特性の変化

DOI Web Site Web Site 参考文献1件

書誌事項

タイトル別名
  • Change in Hydrogen Thermal Desorption Characteristic of Reduced Activation Ferritic/Martensitic Steel with Creep
  • テイホウシャカ フェライトコウ ノ クリープ ニ トモナウ スイソショウオン ダツリ トクセイ ノ ヘンカ

この論文をさがす

抄録

<p>The change in hydrogen thermal desorption characteristic of reduced activation ferritic/martensitic (RAFM) steel for fusion reactor blanket due to creep was investigated to examine the applicability of thermal desorption analysis (TDA) to remaining-life assessment. The hydrogen charging into creep damaged specimens was conducted by means of cathodic electrolysis. The hydrogen-charged samples were subjected to the TDA for the measurement of hydrogen evolution curve. The experimental results revealed that the evolution curve was changed only by creep depending on the test conditions, and the amount of hydrogen desorbed during the analysis (CH) increased with increasing the creep life consumption. A vacancy-type defect and dislocation, which were introduced by the electron beam irradiation and the cold rolling respectively, had a large influence on the desorption characteristic, but they were by no means causes of the change in desorption characteristic with creep. It was also found that the CH was successfully arranged with the parameter derived based on the creep void growth’s law, irrespective of test conditions. The results obtained in this study indicated that the TDA could be a strong tool for the creep damage detection and remaining-life assessment of RAFM steel.</p>

収録刊行物

  • 材料

    材料 70 (2), 140-146, 2021-02-15

    公益社団法人 日本材料学会

参考文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ