溶接残留応力場での下限界値近傍の疲労き裂伝ぱとき裂開閉口挙動の関係

書誌事項

タイトル別名
  • An Explanation for Near-Threshold Fatigue Crack Propagation Behavior in Welded Residual Stress Fields by Crack Closure Phenomenon

この論文をさがす

抄録

Fatigue crack growth rates and threshold for crack propagation were determined for CCT and SEN specimens taken from the butt welded joints in 600 MPa grade steel. The crack opening stress has also been determined by using relation between the elastic compliance and loads. The compressive residual stresses resulted in the decrease of fatigue crack growth rates and the increase or threshold values. These behavior strongly depended on the stress ratio. While, the tensile residual stresses resulted in the increase of fatigue crack growth rates and the decrease of threshold values. These behavior scarcely depended on the stress ratio. The effects of welded residual stresses and stress ratio can be correlated by using the effective stress intensity range concept.

収録刊行物

キーワード

詳細情報 詳細情報について

  • CRID
    1570009752462513536
  • NII論文ID
    110003422713
  • NII書誌ID
    AN1005067X
  • ISSN
    02884771
  • 本文言語コード
    ja
  • データソース種別
    • CiNii Articles

問題の指摘

ページトップへ