Gas Shielded Arc Welding of High-Nitrogen Austenitic Stainless Steel (Report 1)

被引用文献1件

この論文をさがす

抄録

The present paper summarizes the results of investigation on the gas shielded arc welding process on high-nitrogen austenitic stainless steels. High-nitrogen austenitic stainless steel plates (type 316N) were welded by using regular type 316 electrode wire and N_2, Ar, N_2-Ar, N_2-O_2 and N_2-CO_2 mixture shielding gas. The elevated temperature tensile and impact tests on deposited metal specimens were carried out. High-nitrogen austenitic stainless steel weld metals give a tensile strength of about 70 and about 30kg/mm^2 at room temperature and 700℃, respectively. Elongation and reduction of area are not influenced by test temperature and about 15% and about 20% for temperature range room〜700℃ respectively. At impact test, the absorbed energies were not affected by the test temperature and high-nitrogen austenitic stainless steel weld metals made in N_2-Ar mixture shielding gas heve the largest value of absorbed energy of about 16〜18kg-mat test temperature range for room〜700℃. Weld metals made in N_2-CO_2 mixture shielding gas have the smollest value of absorbed energy. From view point of MIG process, high-nitrogen austenitic stainless steel plate is able to be welded by using regular type electrode wire due to using of N_2-Ar mixture shielding gas.

収録刊行物

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

  • CRID
    1571698602231831040
  • NII論文ID
    110006484693
  • NII書誌ID
    AA00867058
  • ISSN
    03874508
  • 本文言語コード
    en
  • データソース種別
    • CiNii Articles

問題の指摘

ページトップへ