Thermal Stability of Microstrucuture and Microhardness in Nanostructured Ni-Cr Alloy Foils Prepared by RF Sputtering Method(Materials, Metallurgy & Weldability)

この論文をさがす

抄録

Nanostructured Ni-Cr binary alloy foils were fabricated by utilizing the RF-magnetron sputtering method and characterization of the foils was performed to examine microstructure, mechanical properties and thermal stability. Each foil was a nanostructured solid solution with an average grain size less than 60nm. Average grain size increased with an increase in Cr content up to 40at%. The microhardness of the foils increased with the solute content up to 5at% and showed the maximum value of 7.0GPa, but then decreased for the further increase of Cr content. The Ni-15at%Cr alloy foil showed no decrease of microhardness up to 773K during isochronal annealing for 7.2ks, but a drastic decrease occurred as the annealing temperature was raised above 773K and the hardness decreased to 2.5GPa at 923K. Abnormal grain growth was observed in the Ni-15at%Cr alloy during isothermal annealing at 973K. The decrease of the microhardness was due to the grain growth during the annealing.

収録刊行物

詳細情報

  • CRID
    1572824502139879168
  • NII論文ID
    110006486136
  • NII書誌ID
    AA00867058
  • ISSN
    03874508
  • 本文言語コード
    en
  • データソース種別
    • CiNii Articles

問題の指摘

ページトップへ