MIG Arc Welding of Magnesium Alloy(Physics, Processes, Instruments & Measurements, INTERNATIONAL SYMPOSIUM OF JWRI 30TH ANNIVERSARY)

Search this article

Abstract

AZ31 magnesium alloy sheet of 1.6mm in the thickness was successfully welded at the high speed of 300cm/min using AZ61 filler wire and DC pulse MIG arc welding. The range of the appropriate welding condition was determined from bead appearance and macrostructure by changing the parameters of the welding current and welding speed. The welded bead was grouped by three-grades ; a burn-through bead, a sufficient penetration and an insufficient penetration bead. The tensile strength of the butt-joint was 250MPa, which was 98% of that of the base metal. The elongation was 6%, much lower than that of base metal of 13%.

Journal

  • Trans. JWRI

    Trans. JWRI 32 39-40, 2003

    Osaka University

Citations (1)*help

See more

References(0)*help

See more

Related Articles

See more

Related Data

See more

Related Books

See more

Related Dissertations

See more

Related Projects

See more

Related Products

See more

Details

  • CRID
    1573668927070019456
  • NII Article ID
    110006486172
  • NII Book ID
    AA00867058
  • ISSN
    03874508
  • Text Lang
    en
  • Data Source
    • CiNii Articles

Report a problem

Back to top