Properties and HR-TEM Observations of Al/ Mild Steel Clad Materials : Development of Clad Materials by Vacuum Roll Bonding and its Characteristics (part 5)

Bibliographic Information

Other Title
  • 純Al/炭素鋼クラッド材の接合部特性と微細構造の観察 : 真空圧延接合法によるクラッド材の製造とその特性(第5報)
  • 純AI/炭素鋼クラッド材の接合部特性と微細構造の観察--真空圧延接合法によるクラッド材の製造とその特性(第5報)
  • ジュンAI タンソ コウ クラッドザイ ノ セツゴウブ トクセイ ト ビサイ コウゾウ ノ カンサツ シンクウ アツエン セツゴウホウ ニ ヨル クラッドザイ ノ セイゾウ ト ソノ トクセイ ダイ5ホウ

Search this article

Abstract

We hold many expectations that aluminum-clad steel will be applied for functional material, structural transition joint for welding steel structure to aluminum structure and so on. In this study we investigated the effects of aluminum purity and/or bonding conditions, which were bonding temperature, reduction rate of aluminum plate thickness (R_<Al>), vacuum degree, on bond tensile strength of aluminum-clad steels produced by the vacuum roll bonding. And also the bond interfaces were observed using a high-resolution transmission electron microscope (RE-TEM). When A1050/SS400 clad materials, which produced at more than 450℃ in bonding temperature, more than 17% in R_<Al> and less than 10 Pa in vacuum degree, were performed in tensile test, they fractured through base metal of the aluminum. The values of bond tensile strength were obtained over 100 MPa. The bond tensile strength of 4N-Al (99.99 mass%Al)/SS400 clad material, which produced at 500℃ in bonding temperature, 20% in R_<Al> and 3 Pa in vacuum degree, was obtained about 80 MPa and test piece fractured through base metal of the aluminum. In the analysis results for bond interface of A1050/SS400 clad materials (500℃ in bonding temperature, 20% in R_<Al> and 3 and 10 Pa in vacuum degree) using a HR-TEM and an electron dispersive spectroscopy (EDS), no intermetallic compound and continuously amorphous phase in thickness from 2 to 3 nm were observed. The composition of the amorphous phase consists of mostly Al, O, Fe and Si. For the bonding interface of 4N-Al/SS400 clad material (500℃ in bonding temperature, 20% in R_<Al> and 3 Pa in vacuum degree), amorphous phase and nano-crystal were observed using HR-TEM. Therefore, it was clarified A1050 and 4N-Al/SS400 clad materials obtained using a vacuum roll bonding were bonded through the amorphous phase.

Journal

Citations (6)*help

See more

References(18)*help

See more

Related Articles

See more

Related Data

See more

Related Books

See more

Related Dissertations

See more

Related Projects

See more

Related Products

See more

Details

Report a problem

Back to top