Fabrication and Characterization of Calcium Silicate Phosphors - Ca<sub>2</sub>SiO<sub>4</sub> and Ca<sub>2</sub>MgSi<sub>2</sub>O<sub>7</sub> -

DOI

Bibliographic Information

Published
2013-07-01
DOI
  • 10.4028/www.scientific.net/msf.761.59
Publisher
Trans Tech Publications, Ltd.

Description

<jats:p>Calcium silicate phosphors, Ca2-xSiO4(CS):Eu3+x, CS:Eu2+x and Ca2-y-zMgSi2O7 (CMS):Eu2+y,Dy3+z were prepared by the solid state reaction. The phases in CS:Eu3+ system were β- and αL’ -types. The fluorescent color under a black-light irradiation was red and the emission spectrum consisted of 590nm(αL’), 615nm(β) and 625nm(αL’) peaks. The emission intensity took a maximum value at x=0.2. The addition of B3+ accelerated the solid solution of Eu3+. The phase in CS:Eu2+ system was β-type only. The fluorescent color was yellow-green(520nm). The emission intensity took a maximum value at x=0.01. The CMS product showed the akermanite phase. The lattice constants of CMS:Eu2+ increased with increasing Eu content, but those became constant at y>0.05. The fluorescent color of CMS:Eu2+ was yellow-green and the emission intensity took a maximum value at y=0.03. In the case of CMS:Eu2+0.03,Dy3+z, the fluorescent color and the afterglow color were same, yellow-green. The emission intensity took a maximum value at z=0.06. The longest afterglow time, 23min., was obtained at z=0.09. The trap depth were 0.64-0.69 eV.</jats:p>

Journal

Details 詳細情報について

Report a problem

Back to top