加工硬化した鋼材の疲労(第5報)

書誌事項

タイトル別名
  • On the Fatigue of Work-Hardened Steel (5th Report)

この論文をさがす

抄録

The Ono type rotational bending fatigue limits are studied about specimens of usual carbon steel after plastically deformed by statical uniform bending moment of about 2~4% maximum strain. The plastic bending produces the residual stress, but the effect of it upon the fatigue strength can not be found. The fatigue fracture 'is always due to the progressive spreading of fatigue crack started at tension side bending, that is, at side having the residual compressive stress. The reason of the fatigue crack starts at tension side is thought to be due to that the fatigue strength of specimen which is not repolished after tensile pre-working, is weaker than that by compressive pre-working of the same degree. (Received December 11, 1952)

資料番号: SA2410140000

収録刊行物

被引用文献 (0)*注記

もっと見る

参考文献 (0)*注記

もっと見る

関連論文

もっと見る

関連研究データ

もっと見る

関連図書・雑誌

もっと見る

関連博士論文

もっと見る

関連プロジェクト

もっと見る

関連その他成果物

もっと見る

詳細情報

ページトップへ