Synthesis and Reversible Li-intercalation Behavior of BaFeO4 films

DOI Web Site Web Site 参考文献6件
  • IDO Hidekazu
    Department of Electronic Chemistry, Interdisciplinary Graduate School of Science and Engineering, Tokyo Institute of Technology
  • HIRAYAMA Masaaki
    Department of Electronic Chemistry, Interdisciplinary Graduate School of Science and Engineering, Tokyo Institute of Technology
  • KANNO Ryoji
    Department of Electronic Chemistry, Interdisciplinary Graduate School of Science and Engineering, Tokyo Institute of Technology

この論文をさがす

抄録

Barium iron oxide containing hexavalent iron (FeVIO42−) was directly synthesized on iron substrates by anodic oxidation using Ba(OH)2 solution. The lithium (de)intercalation properties were investigated using X-ray diffraction, X-ray photoelectron spectroscopy, high-resolution transmission electron microscopy, and electrochemical charge/discharge measurements. A 45 nm thick BaFeO4 film exhibited a discharge capacity of 300 mAh g−1, which is close to the theoretical value of 313 mAh g−1 calculated from the three electron reaction between iron VI and III states.