高炉スラグ細骨材を用いたコンクリートの化学抵抗性に関する研究
書誌事項
- タイトル別名
-
- A Study on Resistance for Chemical Action of Concrete Contained Blast Furnace Slag Fine Aggregate
この論文をさがす
説明
In this study, resistance for chemical action of concrete contained blast furnace slag fine aggregate was examined by soaking specimens in sulfuric acid solution and hydrochloric acid solution. As a result, the concrete contained blast furnace slag could make hard layer of calcium sulfate dehydrate on the concrete surface when the specimen was soaked in the sulfuric acid solution. Therefore, the hard layer reduced carbonation of the concrete. Also carbonation of the concrete contained blast furnace slag could be reduced when the specimen was soaked in the hydrochloric acid solution. It is considered that soft layer between cement paste and aggregate is hard because of latent hydraulic property of the blast furnace slag fine aggregate.
本研究では，化学抵抗性の高いセメント，混和材および高炉スラグ細骨材を組み合わせたコンクリートの硫酸および塩酸に対する抵抗性を，浸漬試験を行い検討した．
収録刊行物
-
- ものつくり大学紀要
-
ものつくり大学紀要 (10), 14-20, 2021
学校法人ものつくり大学
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1050006352474364288
-
- ISSN
- 21853746
-
- 本文言語コード
- ja
-
- 資料種別
- departmental bulletin paper
-
- データソース種別
-
- IRDB