糖蜜を添加したセメント鋳型による鋳造欠陥について
書誌事項
- タイトル別名
-
- Casting Defects Occurable to Cement-Bonded and Molasses-Added Molds
この論文をさがす
説明
This paper is a report of study on the casting defects occurable to cement-bonded and molasses-added mold, concerning to the permeability of mold and the pressure of gas from core in pouring process of cast iron and aluminum alloy. Results are obtained as follows:1) Permeability of the testing sand after 24 hours' drying at room temperature shows 210-290. This figure means that the cement-bonded molds have good permeability. 2) The pressure of gas from core changes under influence of water and molasses. Higher gas pressure caused by higher water content tends to produce more gas-originated defects. 3) Improper decrease of water content tends to cause other type of casting defects, such as rough surface, sand hole, sand inclusion. So, a proper mixing ratio of additions should be selected to produce sound castings; for example, weight ratio of sand 100, cement 10, water 5 ~6, and molasses 3~4, for our experimental conditions, can be recommended.
紀要論文
収録刊行物
-
- 琉球大学理工学部紀要. 工学篇
-
琉球大学理工学部紀要. 工学篇 (6), 1-5, 1973-03
琉球大学理工学部
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1050011251817840000
-
- NII論文ID
- 120004288639
-
- NII書誌ID
- AN00250785
-
- ISSN
- 0387429X
-
- HANDLE
- 20.500.12000/24956
-
- 本文言語コード
- ja
-
- 資料種別
- departmental bulletin paper
-
- データソース種別
-
- IRDB
- CiNii Articles