〈原著論文〉UCST型ノニオン系ポリマーを表面修飾したガラス基板の調製とHeLa細胞の温度刺激はく離

書誌事項

タイトル別名
  • UCSTガタ ノニオンケイ ポリマー オ ヒョウメン シュウショク シタ ガラス キバン ノ チョウセイ ト HeLa サイボウ ノ オンド シゲキ ハクリ
  • Preparation of UCST types of nonion polymer modified glass and thermal stimuli-exfoliation of HeLa cells on the substrate

この論文をさがす

抄録

Poly (acrylamide-co-acrylonitrile)[poly (AAm-co-AN)] with upper critical solution temperature (UCST) was grafted onto a glass substrate by surface initiated atom transfer radical polymerization(SI-ATRP). From the scanning probe microscope(SPM) measurements, poly-(AAm-co-AN) brushes were observed on the glass substrate(g-glass). The contact angle(θ) value of g-glass to water at 26℃ increased from θ=21°(the untreated glass) to θ=69°. On the other hand, that of g-glass at 40℃ decreased from θ=69°to θ=65°. After being HeLa cells attached and proliferated on the g-glass at 30℃ under UCST of poly(AAm-co-AN) burshes, the HeLa cells attached were thermally exfoliated by increasing culture temperature over 37℃ for 30 min in phosphate buffered saline(pH7.4). The % of mechanical and thermal stimuli-exfoliation of attached HeLa cells on the g-glass was about 90% despite of about 10% on untreated glass.

Ⅲ.論文集

Departmental Bulletin Paper

application/pdf

収録刊行物

詳細情報 詳細情報について

問題の指摘

ページトップへ