- <Original Papers>Fundamental Studies on Uranium Oxides.(2) : Equilibria among UO_2,U_4O_9 and U_3O_8 at 500-1,200℃
この論文をさがす
抄録
application/pdf
Oxidation and reduction equilibria among UO_2,U_4O_9 and U_3O_8 were measured with a flow method up to 1,200℃. It was found from the present results that the knowledge about relation-ship among p_<O_2>, O/U ratio and temperature in the 1st report could be extended to higher temperatures, and a new phase diagram of UO_2-U_3O_8 system was proposed. In this temperature and composition range, there are three uranium oxides ; UO_2,U_4O_9 and U_3O_8. UO_2 increases its oxygen solubility with rising temperature above 580℃, and below this temperature, the solubility increases with lowering temperature. The oxygen rich side of this region is heterogeneous and expressed as UO_<2+x>+U_4O_9. Its upper limit was found to be 1,073℃. The temperature dependence of oxygen potential was given by the following equations : 2U_4O_9=8UO_2 (saturated with O)+O_2,log P_<O_2>=-53,158/T+17.059 logT-0.02713T+17.715. Above 800℃ it may be simplified as follows : logP_<O_2>=-21,884/T+11.265. In the composition range of U_4O_9-U_3O_8,it was found to be homogeneous solid solution up to 1,200℃.
紀要類(bulletin)
400672 bytes
収録刊行物
-
- 東北大學選鑛製錬研究所彙報 = Bulletin of the Research Institute of Mineral Dressing and Metallurgy, Tohoku University
-
東北大學選鑛製錬研究所彙報 = Bulletin of the Research Institute of Mineral Dressing and Metallurgy, Tohoku University 16 (2), 109-115, 1961-02-24
東北大學選鉱製錬研究所
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1050282677704878336
-
- NII論文ID
- 110000202200
-
- NII書誌ID
- AN00168425
-
- ISSN
- 0040876X
-
- HANDLE
- 10097/32374
-
- NDL書誌ID
- 9129115
-
- 本文言語コード
- ja
-
- 資料種別
- departmental bulletin paper
-
- データソース種別
-
- IRDB
- NDL
- CiNii Articles