- SiC whisker reinforced Al-Mg-Si alloy composites produced by powder method were extruded at 600℃ by varying angle of dying, and extrudability and mechanical properties of extruded rods were examined. The following results were obtained. (1) Extrusion pressure was lower when the angle of dying was 75 degree. When SiC whisker contents increased, the extrusion pressure was higher. (2) The mechanical properties of the extruded rods were more improved with the increase in SiC whisker contents. (3) The extruded rod of this alloy showed cyclic fibrous structure, and the planes having high degree of texture were (100) [031].
この論文をさがす
抄録
application
SiC whisker reinforced Al-Mg-Si alloy composites produced by powder method were extruded at 600℃ by varying angle of dying, and extrudability and mechanical properties of extruded rods were examined. The following results were obtained. (1) Extrusion pressure was lower when the angle of dying was 75 degree. When SiC whisker contents increased, the extrusion pressure was higher. (2) The mechanical properties of the extruded rods were more improved with the increase in SiC whisker contents. (3) The extruded rod of this alloy showed cyclic fibrous structure, and the planes having high degree of texture were (100) [031].
収録刊行物
-
- 長野工業高等専門学校紀要
-
長野工業高等専門学校紀要 27 1-8, 1993-12-28
長野工業高等専門学校
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1050282812590709760
-
- NII論文ID
- 120005275110
-
- NII書誌ID
- AN00179170
-
- ISSN
- 02861909
-
- NDL書誌ID
- 3846405
-
- 本文言語コード
- ja
-
- 資料種別
- departmental bulletin paper
-
- データソース種別
-
- IRDB
- NDL
- CiNii Articles