- Influence of Solidified Waste Preparing Condition on Leaching Model Parameters of Easily Soluble Substances in Cement Solidified Waste
この論文をさがす
抄録
In order to clarify the relation between cement solidified waste preparing condition and leaching model parameters of easily soluble substances in cement solidified waste, four samples with different addition ratio of cement to fly ash were prepared in cylindrical form by shielding all their surface except top. Tank leaching test was conducted at L/S of 3.3. As the ratio of cement to fly ash increased, porosity of the sample increased from 32% to 46%. As porosity increased, effective diffusion coefficient, De, of Na, K and Cl increased. Furthermore, De/D0 (D0, molecular diffusion coefficient through water) of Na and K had the similar value, but De/D0 of Cl was smaller than these. Porosity of the sample had little effect on a rate constant of surface dissolution, k, and ratio of volume affecting surface dissolution, γ. A region of diffusion control decided from change of De with time and from incline of logti vs logJi didn’t accord with. This result suggested that it was difficult to decide an region of diffusion control by only incline of logti vs logJi.
収録刊行物
-
- 宮崎大学工学部紀要
-
宮崎大学工学部紀要 50 23-31, 2021-09-28
宮崎大学工学部
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1050294518937446528
-
- NII書誌ID
- AA00732558
-
- ISSN
- 05404924
-
- HANDLE
- 10458/00010261
-
- 本文言語コード
- ja
-
- 資料種別
- departmental bulletin paper
-
- データソース種別
-
- IRDB