Low-temperature magnetic behavior of isocubanite from seafloor hydrothermal deposits in the Okinawa Trough

機関リポジトリ (HANDLE) オープンアクセス

この論文をさがす

説明

The characteristic behavior of magnetic remanence correlated with mineralogical textures and composition was observed using low-temperature magnetometry, microscopy, and chemical analysis of three isocubanite samples collected from hydrothermal deposits in the Okinawa Trough and a sample transformed from natural cubanite via heating. Both zero-field remanence acquired at 5 K and field cooling remanence acquired at 300–5 K of all samples sharply decreased with increasing temperature at approximately 100 K. In addition, low-temperature cycling of isothermal remanence at 300 K exhibited a transition at approximately 100 K; remanence increased with decreasing temperature and vice versa. The intensity of remanence at low temperature and sharpness of the transition varied across samples with different compositions and microscopic textures, that is, the presence or absence of chalcopyrite lamellae and their widths. The sample obtained from a hydrothermal chimney, in which the magnetic transition was most clearly observed, was also subjected to X-ray diffraction, Mössbauer spectroscopy, electrical resistivity, and magnetic hysteresis measurements. The obtained results were generally consistent with those reported previously for unnamed mineral CuFe_3S_4 with an ordered cation arrangement. The low-temperature magnetic behavior of isocubanite possibly depends on the degree of cation ordering and can be regarded as an indicator of chemical composition and cooling history. Therefore, low-temperature magnetometry is useful for the detection of isocubanite and a potentially powerful technique for the prompt estimation of its composition and texture, contributing to our understanding of the formation process of hydrothermal deposits.

収録刊行物

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

  • CRID
    1050301684637190144
  • NII書誌ID
    AA00773930
  • ISSN
    14322021
    03421791
  • HANDLE
    2324/7236433
  • 本文言語コード
    en
  • 資料種別
    journal article
  • データソース種別
    • IRDB

問題の指摘

ページトップへ