- Studies on the industrial application of "Shirasu" (Report 4) : effects of Al(H_2PO_4)_3 on the strength of Shirasu mortar bodies
- シラスモルタルの強度におよぼすリン酸アルミニウムの影響
- シラスモルタル ノ キョウド ニ オヨボス リンサン アルミニウム ノ エイキョウ
この論文をさがす
抄録
Shirasu, and slaked lime were mixed with dilute aluminium phorphate water solution and then poured into mold or press molded. The mortar bodies were prepared as follow; mixing ratio of shirasu:slaked lime= 0.5:1, 1:1, 2:1, mixing water 75~148%, addition of Al(H_2PO_4)_3 0.5~2%. Results are as follow; apparent density 2.18~2.39, bulk density 1.35~1.51, apparent porosity 34.1~40.9%, water absorption 66.0~74.3% and bending strength of 28 days curing in the atomsphere 45.2~80.0kg/cm^2. The pressed molded mortar were prepared as follow; mixing ratio of shirasu:slaked lime=0.5:1, 1:1, 2:1, mixing water 50~60, addition of Al(H_2PO_4)_3 0~5.0%, press-molding pressure 50kg/cm^2. Results are as follow; apparent density 2.26~2.49, bulk density 1.44~1.65, apparent porosity 31.8~40.4%, water absorption 19.7~36.3% and compressive strength of 28 days curing in the atomosphere 39.9~88.2kg/cm^2.
収録刊行物
-
- 鹿児島大学工学部研究報告
-
鹿児島大学工学部研究報告 7 43-46, 1967-03
鹿児島大学
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1050564288834640640
-
- NII論文ID
- 120003055883
-
- NII書誌ID
- AN00040363
-
- HANDLE
- 10232/11084
-
- NDL書誌ID
- 8143594
-
- ISSN
- 0451212X
-
- 本文言語コード
- ja
-
- 資料種別
- departmental bulletin paper
-
- データソース種別
-
- IRDB
- NDL
- CiNii Articles