書誌事項
- タイトル別名
-
- ON THE RECRYSTALLIZATION OF SINGLE SOLID SOLUTION ALLOY ( ROLLING AND RECRYSTALLIZATION TEXTURES OF Cr-Ni ALLOY )
- コヨウタイ ゴウキン ノ サイケッショウ Cr-Ni ゴウキン ノ レイカン アツエン シュウゴウ ソシキ ト サイケッショウ シュウゴウ ソシキ ニ ツイテ
この論文をさがす
抄録
This studies were carried out to clarify the rolling and recrystallization behaviors of 20% Cr-Ni alloy. The results are as follows : In the both specimens slow-cooled and quenched during heat treatment before cold rolling, RD//<110> componet appeared in the rolling textures at smaller reduction. In the specimen quenched during heat treatment before cold rolling, preferred orientations of rolling are (001)[110]+(111)[110]+(001)[100]+(112)[111]. Its RD//<<110> compornent tended to decrease after recrystallization and preferred orientations of recrystallization are (001)[100]+(110)[001]+(111)[312]+(411)[148]+(001)[110]. In the recrystallization texture slow-cooled during heat treatment before cold rolling, RD//<110> component diminished at smaller reduction than quenched ones.
収録刊行物
-
- 鹿児島大学工学部研究報告
-
鹿児島大学工学部研究報告 12 47-56, 1970-09
鹿児島大学
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1050564288837602304
-
- NII論文ID
- 120002807011
-
- NII書誌ID
- AN00040363
-
- HANDLE
- 10232/10462
-
- NDL書誌ID
- 8143531
-
- ISSN
- 0451212X
-
- 本文言語コード
- ja
-
- 資料種別
- departmental bulletin paper
-
- データソース種別
-
- IRDB
- NDL
- CiNii Articles