Longitudinal Uniformity of Commercial Bi2223 Tapes Characterized by Scanning Hall-Probe Microscopy

Web Site

この論文をさがす

説明

We investigated remanent field distributions for commercial Bi2223 tapes with length of 1 m and high critical current Ic of 150 A (77 K, self-field) developed by Sumitomo Electric Industries (SEI) Ltd., by scanning Hall-probe microscopy (SHM) with an active area of 50 μm × 50 μm. All tapes are prepared by powder-in-tube process and sintered by controlled-over pressure (CT-OP) processing at final sintering stage. A bare tape and a 3-ply reinforced one with stainless tape laminations were used for measurements. The distribution of remanent field Brz in perpendicular to broader face of a magnetized tape was measured using SHM, at a fixed distance of 0.5 mm away from a tape surface. Although absolute Brz values in a reinforced tape were 10% lower than bare one, the shape of Brz profile along a lateral direction of a tape was hardly affected by reinforcement and uniformly distributed along a length of each tape. Moreover, we cut away 15 cm piece sample from each tape and measured Brz profile before and after double-sided bending with a bending diameter of 30 mm. The results indicated that degradation in both intensity and longitudinal uniformity of Brz for a reinforced tape is much smaller than for a bare one.

収録刊行物

キーワード

詳細情報 詳細情報について

  • CRID
    1050845762354886016
  • NII論文ID
    120005494280
  • ISSN
    10518223
  • Web Site
    https://repo.lib.tut.ac.jp/records/1558
  • 本文言語コード
    en
  • 資料種別
    journal article
  • データソース種別
    • IRDB
    • CiNii Articles

問題の指摘

ページトップへ