Ultrathin SiO 2 layer formed by the nitric acid oxidation of Si (NAOS) method to improve the thermal-SiO 2 /Si interface for crystalline Si solar cells

DOI Web Site Web Site 参考文献34件

書誌事項

公開日
2017-02
資源種別
journal article
権利情報
  • https://www.elsevier.com/tdm/userlicense/1.0/
DOI
  • 10.1016/j.apsusc.2016.06.001
公開者
Elsevier BV

この論文をさがす

説明

Abstract A combination of the nitric acid oxidation of Si (NAOS) method and post-thermal oxidation is found to efficiently passivate the SiO2/n-Si(100) interface. Thermal oxidation at 925 °C and annealing at 450 °C in pure hydrogen atmosphere increases the minority carrier lifetime by three orders of magnitude, and it is attributed to elimination of Si dangling bond interface states. Fabrication of an ultrathin, i.e., 1.1 nm, NAOS SiO2 layer before thermal oxidation and H2 annealing further increases the minority carrier lifetime by 30% from 8.6 to 11.1 ms, and decreased the interface state density by 10% from 6.9 × 109 to 6.3 × 109eV−1 cm−2. After thermal oxidation at 800 °C, the SiO2 layer on the NAOS-SiO2/Si(100) structure is 2.26 nm thick, i.e., 0.24 nm thicker than that on the Si(100) surface, while after thermal oxidation at 925 °C, it is 4.2 nm thick, i.e., 0.4 nm thinner than that on Si(100). The chemical stability results from the higher atomic density of a NAOS SiO2 layer than that of a thermal oxide layer as reported in Ref. [28] (Asuha et al., 2002). Higher minority carrier lifetime in the presence of the NAOS layer indicates that the NAOS-SiO2/Si interface with a low interface state density is preserved after thermal oxidation, which supports out-diffusion oxidation mechanism, by which a thermal oxide layer is formed on the NAOS SiO2 layer.

収録刊行物

参考文献 (34)*注記

もっと見る

関連プロジェクト

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ