Deuterium permeation and thermal behaviors of amorphous silicon carbide coatings on steels
書誌事項
- 公開日
- 2011-10
- 資源種別
- journal article
- 権利情報
-
- https://www.elsevier.com/tdm/userlicense/1.0/
- https://www.elsevier.com/legal/tdmrep-license
- DOI
-
- 10.1016/j.fusengdes.2011.01.036
- 公開者
- Elsevier BV
この論文をさがす
説明
Abstract In this study, deuterium permeation measurements for SS316 and F82H steels coated with amorphous silicon carbide films by radio frequency magnetron sputtering are performed. The driving deuterium pressure dependence of the coated sample shows a large surface contribution. Deuterium trapping in the amorphous structure is suggested by the temporal change in the permeation flux. Permeation reduction factors of 10 3 are achieved with 1.5-μm-thick coated F82H at 723–823 K; however, the coating degraded at 873 K. Cracks are generated in the coating because of the tensile stress derived from a large difference in the thermal expansion between the coating and the steel.
収録刊行物
-
- Fusion Engineering and Design
-
Fusion Engineering and Design 86 (9-11), 2192-2195, 2011-10