An investigation of ductility and microstructural evolution in an Al−3% Mg alloy with submicron grain size

DOI Web Site 被引用文献9件

書誌事項

公開日
1993-11
権利情報
  • https://www.cambridge.org/core/terms
DOI
  • 10.1557/jmr.1993.2810
公開者
Springer Science and Business Media LLC

この論文をさがす

説明

<jats:p>A submicrometer-grained (SMG) Al−3% Mg solid solution alloy, with an initial grain size of ∼0.2 μm, was produced by intense plastic straining. Experiments show that tensile specimens of the SMG alloy exhibit high elongations to failure at low testing strain rates at the relatively low temperature of 403 K. The stress exponent is high (∼7–8) and calculations show deformation is within the region of power-law breakdown. The initial microstructure of the alloy consists of diffuse boundaries between highly deformed grains. At strain rates of ∼10<jats:sup>−4</jats:sup> s<jats:sup>−1</jats:sup> and lower, plastic deformation leads to dynamic recrystallization and the formation of highly nonequilibrium grain boundaries that gradually evolve into a more equilibrated configuration.</jats:p>

収録刊行物

被引用文献 (9)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ