CBD‐Cd<sub>1−<i>x</i></sub>Zn<sub><i>x</i></sub>S thin films and their application in CdTe solar cells
書誌事項
- 公開日
- 2004-02-10
- 権利情報
-
- http://onlinelibrary.wiley.com/termsAndConditions#vor
- DOI
-
- 10.1002/pssb.200304218
- 公開者
- Wiley
この論文をさがす
説明
<jats:title>Abstract</jats:title><jats:p>Composition, optical properties, structure properties, and surface morphology of thin films of Cd<jats:sub>1−<jats:italic>x</jats:italic></jats:sub>Zn<jats:sub><jats:italic>x</jats:italic></jats:sub>S (<jats:italic>x</jats:italic> ≤ 10%) prepared by chemical bath deposition (CBD) are reported. The best cell efficiency was 15.7%. It used a Cd<jats:sub>1−<jats:italic>x</jats:italic></jats:sub>Zn<jats:sub><jats:italic>x</jats:italic></jats:sub>S window layer, was confirmed by NREL (<jats:italic>V</jats:italic><jats:sub>oc</jats:sub> = 840.1 mV, <jats:italic>J</jats:italic><jats:sub>sc</jats:sub> = 24.81 mA/cm<jats:sup>2</jats:sup>, and FF = 75.55%), and had a CTO/ZTO/Cd<jats:sub>0.92</jats:sub>Zn<jats:sub>0.08</jats:sub>S/CdTe cell structure. The use of low zinc concentration in the Cd<jats:sub>1−<jats:italic>x</jats:italic></jats:sub>Zn<jats:sub><jats:italic>x</jats:italic></jats:sub>S layer and interdiffusion between Cd<jats:sub>1−<jats:italic>x</jats:italic></jats:sub>Zn<jats:sub><jats:italic>x</jats:italic></jats:sub>S and CdTe layers were assumed to be the reasons for maintaining high <jats:italic>V</jats:italic><jats:sub>oc</jats:sub> and FF. (© 2004 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)</jats:p>
収録刊行物
-
- physica status solidi (b)
-
physica status solidi (b) 241 (3), 775-778, 2004-02-10
Wiley