Effect of Mold Electromagnetic Stirring and Final Electromagnetic Stirring on the Solidification Structure and Macrosegregation in Bloom Continuous Casting

DOI Web Site Web Site 被引用文献1件
  • Yadong Wang
    School of Metallurgical and Ecological Engineering University of Science and Technology Beijing (USTB) Beijing 100083 China
  • Lifeng Zhang
    State Key Lab of Metastable Materials Science and Technology School of Mechanical Engineering Yanshan University Qinhuangdao 066004 China
  • Wen Yang
    School of Metallurgical and Ecological Engineering University of Science and Technology Beijing (USTB) Beijing 100083 China
  • Sha Ji
    School of Metallurgical and Ecological Engineering University of Science and Technology Beijing (USTB) Beijing 100083 China
  • Ying Ren
    School of Metallurgical and Ecological Engineering University of Science and Technology Beijing (USTB) Beijing 100083 China

抄録

<jats:sec><jats:label /><jats:p>The solidification structure and macrosegregation are investigated in different current intensities of mold electromagnetic stirring (M‐EMS) and final electromagnetic stirring (F‐EMS) by a series of industrial trials during the 20CrMnTi bloom continuous casting (CC) process. With the current intensity of M‐EMS increasing from 100 to 390 A, the deflection angle of columnar dendrites increases from 25.0 to 32.49 deg. With the current intensity of M‐EMS increasing from 0 to 390 A, the equiaxed crystal ratio increases from 20.4% to 25.7% and center porosity varies little. With the increasing current intensity of M‐EMS, the negative segregation in the subsurface and positive segregation in the columnar‐to‐equiaxed transition (CET) zone deteriorate gradually. The M‐EMS has little effect on the center‐positive segregation, and the center‐positive segregation is maintained at 1.37–1.40. With the current intensity of F‐EMS increasing from 0 to 500 A, the equiaxed crystal ratio is within 25.3–25.8%, and the large center porosities disappear instead of numerous fine spots in the equiaxed zone. The degree of center‐positive segregation decreases from 1.48 to 1.30. For the CC process, to obtain a better internal quality of 20CrMnTi bloom, the optimal current intensities of M‐EMS and F‐EMS are 0 and 500 A, respectively.</jats:p></jats:sec>