Improvement in bond behavior and thermal properties of carbon fiber-reinforced polymer strengthened steel structures
書誌事項
- 公開日
- 2021-12
- 資源種別
- journal article
- 権利情報
-
- https://www.elsevier.com/tdm/userlicense/1.0/
- https://www.elsevier.com/legal/tdmrep-license
- http://www.elsevier.com/open-access/userlicense/1.0/
- https://doi.org/10.15223/policy-017
- https://doi.org/10.15223/policy-037
- https://doi.org/10.15223/policy-012
- https://doi.org/10.15223/policy-029
- https://doi.org/10.15223/policy-004
- DOI
-
- 10.1016/j.compstruct.2021.114704
- 公開者
- Elsevier BV
この論文をさがす
説明
Abstract This study focused on the bond strength and environmental durability of carbon fiber-reinforced polymer (CFRP)-strengthened steel structures, by investigating the improvements in the surface treatment of the steel substrate, thermal properties of the epoxy resin, and curing process of the composite. The results showed that the steel–adhesive interfacial bonding behavior can be improved by increasing the surface roughness and using a low-viscosity primer to enhance the wettability. During the initial curing, a lower ambient temperature during the gel time can reduce the porosity of the multi-CFRP laminate. However, raising the initial curing temperature is advantageous for the mechanical and thermal properties of the composite. In addition, the thermal properties of the epoxy matrix were clarified by differential scanning calorimetry tests, based on which isothermal curing degree curves of the system were drawn. The results demonstrated that post-curing at 80 °C is vital for increasing the glass transition temperature, which is also appropriated for the primer. Finally, the moisture and thermal effects on the deterioration of the adhesive joint were examined by conducting short-period aging tests in immersion and wet–dry cyclic environments, during which delamination strength reduction and failure mode transformation were observed.
収録刊行物
-
- Composite Structures
-
Composite Structures 278 114704-, 2021-12
Elsevier BV
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1360294643756938752
-
- ISSN
- 02638223
-
- 資料種別
- journal article
-
- データソース種別
-
- Crossref
- KAKEN
- OpenAIRE